Grade :
|
1Cr18Ni12Mo2Ti 壓力用焊接鋼管。不銹鋼管
|
|
|
|
|
|
|
|
|
Number:
|
X6CrNiMoTi17-12-2
|
|
|
|
|
|
|
|
|
Classification:
|
奧氏體不銹鋼
|
|
|
|
|
|
|
|
|
Density:
|
8 g/cm ?
|
|
|
|
|
|
|
|
|
Standard:
|
|
|
|
|
|
|
|
|
|
EN 10088-2:2005不銹鋼。通用耐腐蝕鋼片/板和帶材交貨技術條件
|
|
|
|
|
|
|
|
|
EN 10088-3:2005不銹鋼。一般用途耐腐蝕鋼的半成品、棒材、線材、型材和光亮產品的交貨技術條件
|
|
|
|
|
|
|
|
|
EN 10028-7:2007壓力用鋼制扁平產品。不銹鋼
|
|
|
|
|
|
|
|
|
EN 10222-5:2000壓力用鋼鍛件。馬氏體、奧氏體和奧氏體-鐵素體不銹鋼
|
|
|
|
|
|
|
|
|
EN 10216-5:2014壓力用無縫鋼管。技術交付條件。不銹鋼管
|
|
|
|
|
|
|
|
|
EN 10217-7:2005壓力用焊接鋼管。不銹鋼管
|
|
|
|
|
|
|
|
|
EN 10296-2:2005機械和一般工程用焊接圓鋼管。不銹鋼。技術交付條件
|
|
|
|
|
|
|
|
|
EN 10253-3:2008對焊管件。無特殊檢驗要求的鍛造奧氏體和奧氏體-鐵素體（雙相）不銹鋼
|
|
|
|
|
|
|
|
|
EN 10253-4:2008對焊管件。有特殊檢驗要求的鍛制奧氏體和奧氏體-鐵素體（雙相）不銹鋼
|
|
|
|
|
|
|
|
|
EN 10272:2007壓力用不銹鋼棒
|
|
|
|
|
|
|
|
|
EN 10263-5:2001冷鐓和冷擠壓用鋼條、棒材和線材。不銹鋼交貨技術條件
|
|
|
|
|
|
|
|
|
EN 10250-4:2000一般工程用開口鋼模鍛件。不銹鋼
|
|
|
|
|
|
|
|
|
EN 10297-2:2005機械和一般工程用無縫圓形鋼管。不銹鋼。技術交付條件
|
|
|
|
|
|
|
|
|
EN 10088-1:2005不銹鋼。不銹鋼清單
|
|
|
|
|
|
|
|
|
EN 10088-5:2009不銹鋼。建筑用耐腐蝕鋼棒材、棒材、線材、型材和光亮產品的交貨技術條件
|
|
|
|
|
|
|
|
|
EN 10088-4:2009不銹鋼。建筑用耐腐蝕鋼片/板和帶材交貨技術條件
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Equivalent grades:
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Chemical composition % of steel X6CrNiMoTi17-12-2 (1Cr18Ni12Mo2Ti ): EN 10088-2-2005
|
|
|
|
|
|
|
|
|
|
Ti = 5 * C to 0.7
|
|
|
|
|
|
|
|
|
|
硫含量的特定范圍可以提供特定性能的改善。對于可加工性，建議并允許將硫含量控制在0.015%至0.030%之間。對于可焊性，建議并允許將硫含量控制在0.008%至0.030%之間。對于可極化性，建議將硫含量控制在最大0.015%。
|
|
|
|
|
|
|
|
|
|
未經買方同意，不得故意將本表中未列出的元素添加到鋼材中，除非對鑄件進行精加工。
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
C
|
Si
|
Mn
|
Ni
|
P
|
S
|
Cr
|
Mo
|
Ti
|
|
max 0.08
|
max 1
|
max 2
|
10.5 - 13.5
|
max 0.045
|
max 0.015
|
16.5 - 18.5
|
2 - 2.5
|
max 0.7
|
|
|
|
|
|
|
|
|
|
|
|
Mechanical properties of steel X6CrNiMoTi17-12-2 (1Cr18Ni12Mo2Ti )
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rm - Tensile strength (MPa) (+A)
|
500-700
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rm - Tensile strength (MPa) (+AT)
|
500-730
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rm - Tensile strength (MPa) (+AT+C)
|
810-850
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rp0.2 0.2% proof strength (MPa) (+A)
|
200-240
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rp0.2 0.2% proof strength (MPa) (+AT)
|
190-210
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
KV - Impact energy (J) transverse, (+A)
|
+20°
|
-196°
|
|
|
|
|
|
|
|
60
|
60
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
KV - Impact energy (J) longitud., (+A)
|
+20°
|
|
|
|
|
|
|
|
|
100
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
A - Min. elongation at fracture (%) (+A)
|
30-40
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
A - Min. elongation at fracture (%) longitud., (+AT)
|
35-45
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Nominal diameter (mm):
|
2 - 50
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Z - Reduction in cross section on fracture (%)
|
60-65
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Brinell hardness (HB): (+A)
|
215
|
|
|
|
|
|
|
|
|
Brinell hardness (HB): (+AT)
|
210
|
|
|
|
|
|
|
|